The effect of adding virgin material or extra stabilizer on the recyclability of polypropylene as studied by multi-cell imaging chemiluminescence and microcalorimetry

• Published in: Polymer degradation and stability 2006-03, Vol.91 (3), p.429-436
• Main Authors: Hamskog, M., Klügel, M., Forsström, D., Terselius, B., Gijsman, P.
• Format: Article
• Language: English
• Subjects: Applied sciences; Chemiluminescence; Exact sciences and technology; Microcalorimetry; Oven ageing; Polymer industry, paints, wood; Polypropylene; Recycling; TAM III; Technology of polymers; Waste treatment
• ISSN: 0141-3910; 1873-2321
• DOI: 10.1016/j.polymdegradstab.2005.02.024

The effect of adding virgin material or new stabilizers on the recyclability of polypropylene (PP) was determined. Stabilized PP was subjected to oven ageing at 130 °C for 100, 250 or 500 h before and after upgrading with virgin material (0, 20, 50, 80 or 100%) or additional stabilizer during reprocessing. The effect of upgrading recycled PP with extra stabilizer or virgin material was determined by measuring the elongation at break, yellowness change, oxidation induction time (OIT) or total luminous intensity (TLI) by chemiluminescence (CL) techniques. Selected specimens were analysed by microcalorimetry (MC). It has been shown that upgrading recycled PP with virgin material was not effective. Adding 80% virgin material did not increase the lifetime more than adding 20% virgin material. This indicates that a small amount of recycled material can induce degradation by contamination. Adding extra stabilizers instead of virgin material was much more effective. Of all techniques used the OIT as determined with CL showed a clear difference in residual stability of differently treated materials and seems to be the most valuable analytical method to determine the recyclability of PP. A comparison between CL and MC shows that MC is sensitive enough for measuring the solid-state oxidation of stabilized PP. Slightly lower OITs were detected by MC probably associated with the static atmosphere used during the measurements. The TLI method is not suitable to determine the degradation state of to be recycled material.