Influence of cathode opening size and wetting properties of diffusion layers on the performance of air-breathing PEMFCs

• Published in: Journal of power sources 2006-03, Vol.154 (2), p.437-447
• Main Authors: Schmitz, A., Tranitz, M., Eccarius, S., Weil, A., Hebling, C.
• Format: Article
• Language: English
• Subjects: Air-breathing PEMFC; Applied sciences; Energy; Energy. Thermal use of fuels; Equipments for energy generation and conversion: thermal, electrical, mechanical energy, etc; Exact sciences and technology; Fuel cells; Geometry variation; Hyrophobic and hydrophilic diffusion layer; Planar PEMFC; Printed circuit board (PCB); Water management
• ISSN: 0378-7753; 1873-2755
• DOI: 10.1016/j.jpowsour.2005.10.070

Air-breathing PEMFCs consist of an open cathodic side to allow an entirely passive supply of oxygen by diffusion. Furthermore, a large fraction of the produced water is removed by evaporation from the open cathode. Gas diffusion layers (GDLs) and the opening size of the cathode have a crucial influence on the performance of an air-breathing PEMFC. In order to assure an unobstructed supply of oxygen the water has to be removed efficiently and condensation in the GDL has to be avoided. On the other hand good humidification of the membrane has to be achieved to obtain high protonic conductivity. In this paper the influence of varying cathodic opening sizes (33%, 50% and 80% opening ratios) and of GDLs with different wetting properties are analysed. GDLs with hydrophobic and hydrophilic properties are prepared by coating of untreated GDLs (Toray ® carbon paper TGP-H-120, thickness of 350 μm). The air-breathing PEMFC test samples are realised using printed circuit board (PCB) technology. The cell samples were characterised over the entire potential range (0–0.95 V) by extensive measurements of the current density, the temperature and the cell impedance at 1 kHz. Additionally, measurements of the water balance were carried out at distinct operation points. The best cell performance was achieved with the largest opening ratio (80%) and an untreated GDL. At the maximum power point, this cell sample achieved a power density of 100 mW cm −2 at a moderate cell temperature of 43 °C. Furthermore, it could be shown that GDLs with hydrophilic or intense hydrophobic properties do not improve the performance of an air-breathing PEMFC. Based on the extensive characterisations, two design rules for air-breathing PEMFCs could be formulated. Firstly, it is crucial to maximise the cathode opening as far as an appropriate compression pressure of the cell assembly and therewith low contact resistance can be assured. Secondly, it is advantageous to use an untreated, slightly hydrophobic GDL.