Wide angle X-ray diffraction and Fourier transform infrared dichroism studies of stretched-recovery-restretched process of polyurethane/clay nanocomposite

An intercalated polyurethane (PU) /clay nanocomposite was prepared by in situ intercalative polymerization. The PU/clay nanocomposite pellet or film samples were stretched‐recovery‐restretched, using selfmade microstretching tools. The changes of the basal spacings of clay and the orientation of pol...

Full description

Saved in:
Bibliographic Details
Published in:Journal of polymer science. Part B, Polymer physics Polymer physics, 2007-03, Vol.45 (6), p.654-660
Main Authors: Chen, Guangming, Ma, Yongmei, Zheng, Xianjun, Xu, Guangyang, Liu, Jun, Fan, Jiaqi, Shen, Deyan, Qi, Zongneng
Format: Article
Language:English
Subjects:
Applied sciences
clay
Composites
Exact sciences and technology
Forms of application and semi-finished materials
infrared dichroism
infrared septroscopy
nanocomposites
Polymer industry, paints, wood
polyurethane
stretched-recovery-restretched
Technology of polymers
wide angle X-ray diffraction
X-ray
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:An intercalated polyurethane (PU) /clay nanocomposite was prepared by in situ intercalative polymerization. The PU/clay nanocomposite pellet or film samples were stretched‐recovery‐restretched, using selfmade microstretching tools. The changes of the basal spacings of clay and the orientation of polymer chain segments during the stretched‐recovery‐restretched process were studied by wide angle X‐ray diffraction (WAXD) and Fourier transform infrared (FTIR) dichoism techniques. The WAXD results show that the basal spacing of clay did not change obviously, indicating that no macromolecular chains entered or moved out of the interlayer space, and the orientations of both hard and soft segments inside the interlayer space did not change obviously, either. The FTIR dichroism tests suggest that outside the interlayer space, the orientation of the hard chain segment increased, decreased, and then increased again during the stretched‐recovery‐restretched process. However, no obvious changes of the degree of orientation of the soft segment were observed during the processes, the slightly orientation might be released during the relaxation process before the measurements. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 654–660, 2007
ISSN:0887-6266
1099-0488
DOI:10.1002/polb.21075