Color- and strength-graded zirconia: Strength, light transmission, and composition

• Published in: The Journal of prosthetic dentistry 2024-06, Vol.131 (6), p.1236.e1-1236.e9
• Main Authors: Maharishi, Anvita, McLaren, Edward A., White, Shane N.
• Format: Article
• Language: English
• Subjects: Color; Dental Materials - chemistry; Dental Stress Analysis; Flexural Strength; Humans; In Vitro Techniques; Light; Materials Testing; Surface Properties; Yttrium - chemistry; Zirconium - chemistry
• ISSN: 0022-3913; 1097-6841
• DOI: 10.1016/j.prosdent.2024.03.015

Natural teeth are graded in terms of translucency and strength. Graded zirconia materials are now available with a higher yttria content on the top or in the enamel zone to increase surface translucency and a lower yttria content on the bottom or in the dentin zone to increase strength. Such materials could provide multiple advantages over uniform materials and reduce the need for porcelain veneering in anterior artificial crowns; however, studies on the properties of these materials are lacking. The purpose of this in vitro study was to measure and compare the biaxial flexural strength, percentage light transmission, elemental content, and phase content of zones within and among color graded zirconia blocks and color- and strength-graded zirconia blocks. Disks of a color graded material (Katana STML) and a strength- and color-graded material (IPS e.max ZirCAD Prime) were fabricated (Zircom Furnace). Biaxial flexural strength was measured using a piston-on-3-ball test in a universal testing machine (n=10). Absolute light transmission was measured with a spectrophotometer. Elemental compositions were quantified for 3 zones in each of the 2 zirconia materials using X-ray fluorescence analysis. Zirconia phase fractions were quantified for 3 zones using X-ray diffraction analysis (XRD). Where appropriate, 2-way ANOVA, 1-way ANOVA, and Tukey multiple pairwise comparison testing were used to determine which of the 6 zones differed from one another (α=.05). The color-graded zirconia exhibited gradients in light transmission and differences in phase content in the 3 zones measured. The color- and strength-graded zirconia exhibited gradients in light transmission, biaxial flexural strength, elemental composition, and phase content in the 3 zones measured. The bottom, dentin, or intaglio layer of a strength graded zirconia material was substantially stronger than all other zones of either material (P