The Impact of Silver Diamine Fluoride and Potassium Iodide Treatment on Microtensile Bonds Strength of Composite Restoration for Carious Dentin in Primary and Permanent Teeth and Its Potential Color Changes: An In Vitro Study

• Published in: European journal of dentistry 2024-11
• Main Authors: Shaheen, Sarah D, Esmaeil, Doaa A M, Ghobar, Somaia
• Format: Article
• Language: English
• ISSN: 1305-7456; 1305-7464
• DOI: 10.1055/s-0044-1791684

This study aims to examine the effects of silver diamine fluoride and potassium iodide (SDF/KI) treatment on the possible color changes and the microtensile bond strength of composite restorations to carious dentin in different dentitions.  A total of 48 sound human teeth were utilized in this study. Twenty-four primary molar teeth were divided into two groups. Each group has 12 teeth; group 1 received no pretreatment, while group 2 received SDF/KI treatment. Also, 24 permanent premolar teeth were divided into two groups. Group 3 received no pretreatment, and group 4 received SDF/KI treatment. For 7 days at 25 °C, every sample was submerged in a demineralizing solution. Following the manufacturer's guidelines for SDF/KI treatments, exposed dentin surfaces were promptly preserved in artificial saliva (pH 7.4) for 14 days. On the prepared teeth surfaces of the nontreated groups, deionized water was administered rather than SDF/KI. A self-etching bonding agent was used, and a 4-mm-thick composite restoration was constructed. Evaluations were conducted on color measurement, microtensile bond strength, and mode of failure.  The groups were compared using a one-way analysis of variance test, and a post hoc test was used for pairwise comparisons.  Regarding color measurement, in deciduous dentition, there were no statistically significant differences between the groups. Additionally, there is no discernible variation in Δ values among various pretreatment groups in the permanent dentition. Microtensile bond strength did not differ significantly between permanent and deciduous teeth.  A 14-day delay in the application of composite restoration can successfully conceal the color of SDF/KI without compromising the microtensile bond strength.