Thermally and optically induced irreversible changes in some Ge–As–S amorphous thin films
Thermally and optically induced irreversible changes in the optical gap and refractive index were studied for sulphur rich, nearly stoichiometric and sulphur poor Ge–As–S amorphous films prepared by thermal evaporation. For films studied the optical gap in the virgin state decreases from 2.55 9 (Ge...
Saved in:
Published in: | Materials chemistry and physics 2008-08, Vol.110 (2), p.322-327 |
---|---|
Main Authors: | , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Thermally and optically induced irreversible changes in the optical gap and refractive index were studied for sulphur rich, nearly stoichiometric and sulphur poor Ge–As–S amorphous films prepared by thermal evaporation. For films studied the optical gap in the virgin state decreases from 2.55
9 (Ge
0.121As
0.172S
0.707) to 1.63
2
eV (Ge
0.254As
0.294S
0.452) and simultaneously the refractive index increases from 2.21 to 2.87, respectively. The most sensitive composition to illumination seems to be nearly stoichiometric film (Ge
0.153As
0.201S
0.646), where the blue shift of the gap is observed close to 150
meV. Sulphur poor film (Ge
0.254As
0.294S
0.452) was found insensitive to illumination. Highest thermally induced blue shift of the gap, close to 250
meV, we observed just for Ge
0.254As
0.294S
0.452 film and for this film it was observed also nearly “giant” decrease in refractive index from 2.85 to 2.42. The behaviour of Ge
0.254As
0.294S
0.452 film is qualitatively discussed using the concept of network rigidity (insensitivity to illumination) and assuming thermally induced changes in bonding arrangement (refractive index changes). |
---|---|