Crystal structure and electrical resistivity studies of Dy ( Mn 0.4 − x Co x Fe 0.6 ) 2 intermetallics
Synthesis and X-ray analysis (300 K) of a new Dy ( Mn 0.4 − x Co x Fe 0.6 ) 2 series were performed. The lattice parameter is considerably reduced with x. Electrical resistivity for the Dy ( Mn 0.4 − x Co x Fe 0.6 ) 2 intermetallic series was measured in a wide temperature range and the parameters c...
Saved in:
Published in: | Journal of alloys and compounds 2008-07, Vol.459 (1), p.13-17 |
---|---|
Main Authors: | , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Synthesis and X-ray analysis (300 K) of a new
Dy
(
Mn
0.4
−
x
Co
x
Fe
0.6
)
2
series were performed. The lattice parameter is considerably reduced with
x. Electrical resistivity for the
Dy
(
Mn
0.4
−
x
Co
x
Fe
0.6
)
2
intermetallic series was measured in a wide temperature range and the parameters characterising the dependence of resistivity on temperature and composition were determined. The magnetic part of the resistivity was used to estimate Curie temperatures. The Curie temperature
T
C
is strongly increased as a result of Mn/Co substitution. The obtained
T
C
-results are related to the data known for the
Dy
(
Mn
1
−
x
Fe
x
)
2
and
Dy
(
Fe
1
−
x
Co
x
)
2
series. |
---|---|