Inhibition of mild steel corrosion in acidic medium using synthetic and naturally occurring polymers and synergistic halide additives

• Published in: Corrosion science 2008-07, Vol.50 (7), p.1998-2006
• Main Authors: Umoren, S.A., Ogbobe, O., Igwe, I.O., Ebenso, E.E.
• Format: Article
• Language: English
• Subjects: A. Mild steel; A. Polymers; Applied sciences; Corrosion; Corrosion environments; Corrosion inhibition; Corrosion prevention; Exact sciences and technology; Halides; Metals. Metallurgy; Synergism
• ISSN: 0010-938X; 1879-0496
• DOI: 10.1016/j.corsci.2008.04.015

The corrosion inhibition of mild steel in H 2SO 4 in the presence of gum arabic (GA) (naturally occurring polymer) and polyethylene glycol (PEG) (synthetic polymer) was studied using weight loss, hydrogen evolution and thermometric methods at 30–60 °C. PEG was found to be a better inhibitor for mild steel corrosion in acidic medium than GA. The effect of addition of halides (KCl, KBr and KI) was also studied. Results obtained showed that inhibition efficiency ( I%) increased with increase in GA and PEG concentration, addition of halides and with increase in temperature. Increase in inhibition efficiency ( I%) and degree of surface coverage ( θ) was found to follow the trend Cl − < Br − < I − which indicates that the radii and electronegativity of the halide ions play a significant role in the adsorption process. GA and PEG alone and in combination with halides were found to obey Temkin adsorption isotherm. Phenomenon of chemical adsorption is proposed from the trend of inhibition efficiency with temperature and values Δ G ads 0 obtained. The synergism parameter, S I evaluated is found to be greater than unity indicating that the enhanced inhibition efficiency caused by the addition of halides is only due to synergism.