Gas permeability reduction in PEEK film: Comparison of tetrahedral amorphous carbon and titanium nanofilm coatings

[Display omitted] ► Nanofilm coatings were applied to polyetheretherketone (PEEK) to assess the potential reduction in permeability. ► Titanium or tetrahedral amorphous carbon coatings applied to PEEK reduced the permeability to helium. ► A maximum reduction in permeability of 83% was achieved with...

Full description

Saved in:
Bibliographic Details
Published in:Journal of membrane science 2011-08, Vol.378 (1), p.265-271
Main Authors: Amanat, Negin, Nicoll, Alexander F., Ruys, Andrew J., McKenzie, David R., James, Natalie L.
Format: Article
Language:English
Subjects:
Chemistry
Colloidal state and disperse state
Exact sciences and technology
General and physical chemistry
Membranes
PEEK
Permeability
Thin film coating
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:[Display omitted] ► Nanofilm coatings were applied to polyetheretherketone (PEEK) to assess the potential reduction in permeability. ► Titanium or tetrahedral amorphous carbon coatings applied to PEEK reduced the permeability to helium. ► A maximum reduction in permeability of 83% was achieved with a 100 nm thick titanium coating. ► Titanium coating outperformed tetrahedral amorphous carbon coating. ► Carbon coatings were covered in a network of microcracks, which were more permeable than the pinholes seen in the titanium coating. The reduction of helium gas permeability through polyetheretherketone (PEEK) microfilm (250 μm) coated with titanium (Ti) or tetrahedral amorphous carbon (ta-C) nanofilm was investigated. Two morphologies of PEEK film were used (amorphous and semi-crystalline), and four thicknesses of nanofilm were deposited (5, 20, 50, or 100 nm). Both types of nanofilm coatings reduced the overall permeability of the PEEK film, with the greatest permeability reduction of ∼83% seen for the 100 nm Ti coating on semi-crystalline PEEK. Defects were identified in both types of coating; however the nature of the defects was different. The ta-C coatings exhibited a network of microcracks, while pinholes were present in the Ti coatings. The defects in both coatings were considered the dominant path for gas flow. Overall, Ti performed better than ta-C with regard to permeability reduction, and Ti also demonstrated a correlation between coating thickness and permeability reduction.
ISSN:0376-7388
1873-3123
DOI:10.1016/j.memsci.2011.05.019