Post deposition annealing temperature effect on silicon quantum dots embedded in silicon nitride dielectric multilayer prepared by hot-wire chemical vapor deposition

The preparations of the 20-period of a Si quantum dot (QD)/SiN x multilayer in a hot-wire chemical vapor deposition (HWCVD) chamber is presented in this paper. The changes in the properties of Si-QDs after the post deposition annealing treatment are studied in detail. Alternate a-Si:H and SiN x laye...

Full description

Saved in:
Bibliographic Details
Published in:Thin solid films 2009-04, Vol.517 (12), p.3488-3491
Main Authors: Panchal, A.K., Solanki, C.S.
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The preparations of the 20-period of a Si quantum dot (QD)/SiN x multilayer in a hot-wire chemical vapor deposition (HWCVD) chamber is presented in this paper. The changes in the properties of Si-QDs after the post deposition annealing treatment are studied in detail. Alternate a-Si:H and SiN x layers are grown in a single SiN x deposition chamber by cracking SiH 4, and SiH 4 + NH 3, respectively at 250 °C. The as-deposited samples are annealed in the temperature range of 800 °C to 950 °C to grow Si-QDs. All the samples are characterized by confocal micro Raman, transmission electron microscope (TEM), and photoluminescence (PL) to study the changes in the film structures after the annealing treatment. The micro Raman analysis of the samples shows the frequency line shifting from 482 cm − 1 to 500 cm − 1 indicating the Si transition from an amorphous to a crystalline phase. The TEM micrograph inspection indicates the formation of Si-QDs of size 3 to 5 nm and a density of 5 × 10 12/cm 2. The high resolution TEM micrographs show an agglomeration of Si-QDs with an increase in the annealing temperature. The PL spectra show a peak shifting from 459 nm to 532 nm with increasing the annealing temperature of the film.
ISSN:0040-6090
1879-2731
DOI:10.1016/j.tsf.2009.01.080