Grain refinement and plastic formability of Mg-14Li-1Al alloy

Al-5Ti-1B master alloy was added into Mg-14Li-1Al（LA141）alloy and then LA141 sheets were prepared by extrusion and cold rolling.The effect of the addition level of Al-5Ti-1B master alloy on the grain size of LA141 alloy was investigated as well as the effects of the total reduction of cold rolling a...

Full description

Saved in:
Bibliographic Details
Published in:Transactions of Nonferrous Metals Society of China 2010-07, Vol.20 (B07), p.503-507
Main Author: 蒋斌 殷恒梅 李瑞红 高亮
Format: Article
Language:English
Subjects:
Alloying additive
Aluminum base alloys
Al合金
Annealing
Cold rolling
grain refinement
Grains
Magnesium base alloys
Master alloys
Mg-14Li-1Al alloy
plasticity formability
Reduction
sheet
中间合金
塑料成形
微观结构
晶粒尺寸
晶粒细化
最佳加入量
退火温度
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Al-5Ti-1B master alloy was added into Mg-14Li-1Al（LA141）alloy and then LA141 sheets were prepared by extrusion and cold rolling.The effect of the addition level of Al-5Ti-1B master alloy on the grain size of LA141 alloy was investigated as well as the effects of the total reduction of cold rolling and the annealing temperature on microstructure,mechanical properties and plastic formability of the LA141 sheets.The results show that the optimal addition level of Al-5Ti-1B master alloy into LA141 alloy is 1.25%（mass fraction）and LA141 alloy has the finest grains.With the increase of the total reduction of cold rolling,the grains of the as-rolled LA141 sheets were flattened gradually.A proper anneal temperature of 200℃ is obtained for the cold rolled LA141 sheets. Under this condition,microstructure of the LA141 sheets consists of fine and uniform equiaxed grains and has higher Erichsen cupping index（IE）.
ISSN:1003-6326
DOI:10.1016/S1003-6326(10)60527-4