Thickness Dependence of Critical Current Density in MgB2 Films Prepared by Thermal Evaporation Method

• Published in: Journal of superconductivity and novel magnetism 2011-01, Vol.24 (1-2), p.523-527
• Main Authors: Yakinci, Z. D., Aydoğdu, Y.
• Format: Article
• Language: English
• Subjects: Aluminum oxide; Borides; Characterization and Evaluation of Materials; Condensed Matter Physics; Condensed matter: electronic structure, electrical, magnetic, and optical properties; Critical current density; Critical currents; Deposition; Evaporation; Exact sciences and technology; High-tc films; Magnesium; Magnesium compounds; Magnetic Materials; Magnetism; Original Paper; Physics; Physics and Astronomy; Properties of type I and type II superconductors; Strongly Correlated Systems; Superconducting films and low-dimensional structures; Superconductivity
• ISSN: 1557-1939; 1557-1947
• DOI: 10.1007/s10948-010-0985-4

MgB 2 films with the thickness of 350 to 1150 nm have been prepared on the Al 2 O 3 (001) single crystal substrates from high purity B and Mg powder by the thermal evaporation method. Films were then heat treated ex-situ under Mg vapor at 950 °C to achieve actual MgB 2 stoichiometry. Thickness of the films, so the deposition time, was varied to investigate its influence on critical current density of the films. The films fabricated were analyzed by means of microstructural, transport, and magnetic properties. The best T c and T zero values were obtained to be 39.5 K and 38 K, respectively, and decreased with increasing the thickness. We found that the critical current density of the films prepared is highly thickness dependent. The maximum value was calculated to be 3.18×10 6  A cm −2 at 10 K and zero field for 1150 nm thick films but dropped drastically by thickness.