Soft magnetic properties of nanocrystalline amorphous HITPERM films and multilayers

• Published in: IEEE transactions on magnetics 2001-07, Vol.37 (4), p.2239-2241
• Main Authors: Huang, M.-Q., Hsu, Y.-N., McHenry, E., Laughlin, D.E.
• Format: Article
• Language: English
• Subjects: Amorphous materials; Coercive force; Coercivity; Condensed matter: electronic structure, electrical, magnetic, and optical properties; Couplings; Exact sciences and technology; Ferrous alloys; Hysteresis; Iron; Joining; Magnetic films; Magnetic multilayers; Magnetic properties; Magnetic properties and materials; Magnetic properties of monolayers and thin films; Magnetic properties of surface, thin films and multilayers; Multilayers; Physics; Saturation magnetization; Semiconductor films; Silicon dioxide; Stepped; Temperature
• ISSN: 0018-9464; 1941-0069
• DOI: 10.1109/20.951135

Amorphous precursors to HITPERM (Fe, Co)-Zr-B-Cu (a-HITPERM) films and a-HITPERM/SiO/sub 2/ multilayer films have been deposited on glass or Si substrates by a rf sputtering system with a target of composition (Fe/sub 0.7/Co/sub 0.3/)/sub 88/Zr/sub 7/B/sub 4/Cu/sub 1/. It was found that the a-HITPERM single layer film with a thickness of 100 mm possessed good soft magnetic properties with a saturation magnetization of 4/spl pi/M/sub s//spl ges/14 kG and a coercivity of H/sub c//spl sim/0.9 Oe at room temperature. Hc increases from 0.9 Oe to 25 Oe when the him thickness increases from 100 to 150 nm. To obtain excellent soft magnetic properties at larger thicknesses, a-HITPERM/SiO/sub 2/ multilayer films have been synthesized. In these, H/sub c/ drops from 25 Oe (single layer) to 0.25 Oe (multilayers) with the same total a-HITPERM thickness. The intervening SiO/sub 2/ layers play an important role in reducing the coercivity. Experimental results show the optimum thickness for SiO/sub 2/ was 2-4 nm. M-H loops for the multilayers films exhibit pronounced two step magnetization reversal processes for temperatures between 5 and 25 K. This behavior can be attributed to magneto-static coupling between a-HITPERM layers and sequential switching of the layers. The coupling exhibits itself in a blocked phenomenon with wide (stepped) hysteresis curves for T25 K. The effects of magneto-static coupling on the magnetic properties of a-HITPERM/SiO/sub 2/ films will be discussed.