The effect of irradiation on tensile properties and fracture toughness of CuCrZr and CuCrNiSi alloys

This paper deals with the effect of irradiation on tensile properties and fracture toughness of CuCrZr and CuCrNiSi alloys, considered for use in some in-vessel components of ITER, where a combination of high strength and heat conduction is essential. The heat treatments were: –CuCrZr, quenching in...

Full description

Saved in:
Bibliographic Details
Published in:Journal of nuclear materials 2011-10, Vol.417 (1-3), p.908-911
Main Authors: Kalinin, G.M., Artyugin, A.S., Yvseev, M.V., Shushlebin, V.V., Sinelnikov, L.P., Strebkov, Yu.S.
Format: Article
Language:English
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This paper deals with the effect of irradiation on tensile properties and fracture toughness of CuCrZr and CuCrNiSi alloys, considered for use in some in-vessel components of ITER, where a combination of high strength and heat conduction is essential. The heat treatments were: –CuCrZr, quenching in water after annealing at 950°С, cold worked 40–45%, and aged at 475–500°С for 3h.–CuCrNiSi, quenching in water after annealing at 980°С and aged for 4h at 460°С. Specimens were irradiated in the IVV-2 reactor at ∼200°С and with irradiation damage of 0.15 and 0.27dpa. Post-irradiation tests were carried out to assess the tensile properties and fracture toughness of the materials. The tests results show that CuCrNiSi has better strength and retains higher ductility after irradiation, but has somewhat lower crack resistance than CuCrZr.
ISSN:0022-3115
1873-4820
DOI:10.1016/j.jnucmat.2011.02.036