Non-Destructive Examination for Cavitation Resistance of Talc-Based Refractories with Different Zeolite Types Intended for Protective Coatings

• Published in: Materials 2023-08, Vol.16 (16), p.5577
• Main Authors: Vlahović, Milica, Alil, Ana, Devečerski, Aleksandar, Živojinović, Dragana, Volkov-Husović, Tatjana
• Format: Article
• Language: English
• Subjects: Analysis; Cavitation; Cavitation erosion; Cavitation resistance; Ceramic materials; Ceramics; Composite materials; Diameters; Energy consumption; Failure analysis; Flue gas; Fluid flow; Furnaces; Gases; High temperature; Hot pressing; Image analysis; Image degradation; Metals; Methods; Modulus of elasticity; Nondestructive testing; Plasma sintering; Principal components analysis; Protective coatings; Refractories; Refractories industry; Service life; Talc; Turbines; Ultrasonic methods; Variables; Water levels; Zeolites
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma16165577

In many industrial processes that include fluid flow, cavitation erosion of different engineering structures (pumps, turbines, water levels, valves, etc.) during their operation is expected. Metallic, ceramic, and composite materials are usual candidates considered for application in such extreme conditions. In this study, the idea is to synthesize refractory ceramic material based on talc with the addition of zeolite for utilization as protective coatings in cavitating conditions. Two talc-based refractories with zeolites from two Serbian deposits were produced. The behaviors of the samples in simulated cavitation conditions were examined by an advanced non-destructive methodology consisting of monitoring mass loss and surface degradation using image analysis compiled with principal component analysis (PCA), interior degradation by ultrasonic measurements, and the microstructure by a scanning electron microscope (SEM). Lower mass loss, surface degradation level, and modeled strength decrease indicated better cavitation resistance of the sample with Igros zeolite, whereby measured strength values validated the model. For the chosen critical strength, the critical cavitation period as well as critical morphological descriptors, Area and Diameter (max and min), were determined. A Young’s elasticity modulus decrease indicated that surface damage influence progressed towards interior of the material. It can be concluded that the proposed methodology approach is efficient and reliable in predicting the materials’ service life in extreme conditions.