Role of the Coreactant on the Dual-Source Behavior of Lithium Hexamethyldisilazide for ALD Li-Containing Films

Atomic layer deposition (ALD) of Li-containing thin films is deemed as highly relevant for the development of next-generation Li-ion batteries. Lithium hexamethyldisilazide (LiHMDS), as Li-containing precursor, is preferred over the widely used lithium tert-butoxide because of its lower melting poin...

Full description

Saved in:
Bibliographic Details
Published in:Journal of physical chemistry. C 2024-11, Vol.128 (46), p.19638-19647
Main Authors: Pieters, M. J., Bartel, L., van Helvoirt, C., Creatore, M.
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Atomic layer deposition (ALD) of Li-containing thin films is deemed as highly relevant for the development of next-generation Li-ion batteries. Lithium hexamethyldisilazide (LiHMDS), as Li-containing precursor, is preferred over the widely used lithium tert-butoxide because of its lower melting point of 70 °C. However, the presence of silyl groups in the LiHMDS chemical structure can result in the undesired incorporation of Si in the film. Therefore, understanding the reaction mechanism of LiHMDS is required to control its dual-source behavior and grow Si-free Li-containing thin films. For this purpose LiHMDS was combined with O2 plasma or water as coreactant. In situ spectroscopic ellipsometry (SE) and X-ray photoelectron spectroscopy (XPS) revealed that using O2 plasma as coreactant results in linear growth and Si-containing films, whereas using H2O as coreactant leads to fast, nonsurface-reaction-limited growth and Si-free films. To shed light on the role of the coreactant on the reaction mechanism of LiHMDS, in situ studies by time-resolved quadrupole mass spectrometry (QMS) were performed on the O2 plasma and H2O-based ALD processes. Measurements taken during full ALD cycles and half-cycles were carefully compared to identify which half-cycle surface reaction products lead to silicon incorporation in the film. The QMS results of the LiHMDS + H2O process showed that LiHMDS both chemisorbs and physisorbs. Furthermore, it is concluded that Si incorporation occurs during the O2 plasma step, when the physisorbed ligands are combusted and Si-containing products are redeposited. This work also demonstrates that the incorporated Si can be abstracted from the film by means of a H2 plasma step following the O2 plasma step. These insights on the role of the coreactant in the synthesis of Li-containing films contribute to the development of LiHMDS-based ALD processes for Li-ion battery applications.
ISSN:1932-7447
1932-7455
DOI:10.1021/acs.jpcc.4c05987