Comparison of compressive strength among three different intracanal post materials in primary anterior teeth: An in vitro study

• Published in: European journal of dentistry 2016-10, Vol.10 (4), p.464-468
• Main Authors: Nilavarasan, Nilavu, Hemalatha, R., Vijayakumar, R., Hariharan, V. S.
• Format: Article
• Language: English
• Subjects: Analysis; Glass products; Original; Original Article
• ISSN: 1305-7456; 1305-7464
• DOI: 10.4103/1305-7456.195181

ABSTRACT Objective: The objective of our study was to compare the fracture resistance and the mode of failure among three different post materials in primary anterior teeth. Materials and Methods: A total of sixty extracted primary anterior teeth were selected for the study. The samples were divided into three groups of twenty teeth each: Group I (Ribbond), Group II (Omega loop), and Group III (Glass fiber post). Pulp therapy was followed by intracanal post and crown buildup. The samples were mounted in self-cure acrylic and subjected to compressive strength test using universal testing machine (Instron). The maximum force at which the tooth fractured was recorded. Results: The values were subjected to one-way analysis of variance. The mean compressive strength values of Ribbond, omega loop, and glass fiber post were found to be 83.25 N, 61.60 N, and 75.55 N, respectively. The P value was found to be 0.220. Conclusion: Group I (Ribbond) showed the highest fracture resistance values followed by Group III (Glass fiber post) and Group II (Omega loop). Although there is difference in mean values, they were nonsignificant.