Effect of Different Irrigants Applied After Post Space Preparation on Push-Out Bond Strength of a Self-Etch Resin Cement

• Published in: Journal of dentistry (Tehran, Iran) Iran), 2018-07, Vol.15 (4), p.222-229
• Main Authors: Jalali, Hamid, Farid, Farzaneh, Kulivand, Sudabeh, Nokar, Saeed, Dadgar, Kosar
• Format: Article
• Language: English
• Subjects: Original
• ISSN: 1735-2150; 2008-2185

The aim was to investigate the effect of intracanal irrigants and agents on the bond strength of intraradicular fiber posts to dentin. Root canals of 72 decoronated single-rooted premolars were cleaned, shaped, and obturated with gutta-percha and AH26. The specimens were incubated at 37°C and 100% humidity for seven days. Next, the coronal 10 mm of the canals were prepared to receive size 2 D.T. Light fiber post, and the specimens were randomly allocated into six groups according to the irrigants used after post space preparation: normal saline (control group), 5.25% sodium hypochlorite (NaOCl)/15 seconds, 17% ethylenediaminetetraacetic acid (EDTA)/60 seconds, 2% chlorhexidine (CHX)/5 minutes, MTAD/5 minutes, and acid-etching/15 seconds. All canals were rinsed with normal saline and dried. Fiber posts were cemented using Panavia F2.0. After 24 hours, two mid-root slices of 1mm thickness were obtained from each specimen. Push-out bond strength test was performed in a universal testing machine at 0.5mm/minute. The maximum applied load was recorded, and the bond strength was calculated in megapascal (MPa). Data were analyzed by one-way analysis of variance (ANOVA) and Tukey's test. The mean shear bond strengths of etched (53.21±12.11 MPa), MTAD (52.47±14.75 MPa) and EDTA (49.08±10.19 MPa) groups were significantly higher than that of the control group (39.82±10.04 MPa). The difference was marginally significant for CHX group (49.8±13.57 MPa) and not significant for NaOCl group (47.15±17.64 MPa). Etching or irrigating the root canals with MTAD or EDTA after post space preparation increases the bond strength of Panavia F2.0 to dentin.