Analysis of resistance to bending of metal electroconductive layers deposited on textile composite substrates in PVD process

In the article a description of the behaviour of metallic layers created in the process of physical vacuum deposition on a composite textile substrates during their cyclical bending process is presented. Either the results of experimental research or the theoretical considerations of changes in the...

Full description

Saved in:
Bibliographic Details
Published in:Scientific reports 2020-05, Vol.10 (1), p.8310-8310, Article 8310
Main Authors: Korzeniewska, Ewa, De Mey, Gilbert, Pawlak, Ryszard, Stempień, Zbigniew
Format: Article
Language:English
Subjects:
3-D printers
639/166/987
639/301/930/12
Composite materials
Electronics
Experimental research
Gold
Humanities and Social Sciences
Materials fatigue
Metal fatigue
multidisciplinary
Polymers
Science
Science (multidisciplinary)
Screen printing
Textiles
Vacuum
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:In the article a description of the behaviour of metallic layers created in the process of physical vacuum deposition on a composite textile substrates during their cyclical bending process is presented. Either the results of experimental research or the theoretical considerations of changes in the structure resistance as a function of the number of fatigue cycles are presented. It was confirmed mathematically that at the beginning of the bending process, in the case of a small number of bends, single cracks appear on the surface of the layer. After exceeding a certain number of bends, the nature of defects on the surface of the layer changes and the dominating mechanism of changes is the widening and elongation of already existing cracks. It has been confirmed mathematically that changes in resistance in these cases depend respectively on the number of bending cycles and next on quadratic value of number of cycles. A correspondence between the mathematical description and experimental results was obtained.
ISSN:2045-2322
2045-2322
DOI:10.1038/s41598-020-65316-2