In Vivo Corrosion Behavior of Biodegradable Magnesium Alloy by MAF Treatment

Coating treatment plays an irreplaceable role in propelling the clinical application of magnesium alloys. This experiment was designed in order to observe the anticorrosion behavior of magnesium fluoride coating in rats. The MgF2 layer was prepared on the surface of AZ31 magnesium alloy in saturated...

Full description

Saved in:
Bibliographic Details
Published in:Scanning 2021, Vol.2021, p.1-9
Main Authors: Gao, Xinzhe, Dai, Chun Yu, Jia, Qi, Zhai, ChuanYao, Shi, HaoYu, Yang, Yifan, Zhao, Bing Cheng, Cai, HongXin, Lee, Eui-Seok, Jiang, Heng Bo
Format: Article
Language:English
Subjects:
Biocompatibility
Biodegradability
Coating
Corrosion prevention
Corrosion rate
Corrosion resistance
Corrosion tests
Electrodes
Electrolytes
Experiments
Fluorides
Fluorination
Magnesium alloys
Magnesium base alloys
Magnesium fluorides
Medical research
Morphology
Muscles
Scanning electron microscopy
Titanium alloys
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Coating treatment plays an irreplaceable role in propelling the clinical application of magnesium alloys. This experiment was designed in order to observe the anticorrosion behavior of magnesium fluoride coating in rats. The MgF2 layer was prepared on the surface of AZ31 magnesium alloy in saturated NH4HF2 solution by microarc fluorination (MAF) at 190 V. The cross-sectional SEM, EDS, and XRD analysis indicated that the alloy surface was covered with MgF2. Meanwhile, SEM observation was used to compare the magnesium alloy samples before and after treatment, and it was found that the samples after coating were flatter and smoother. Two sets of experiments were carried out with the subjects, 6-week-old male rats. So that the untreated AZ31 samples and the microarc fluorinated AZ31 samples could be buried under the muscle layer individually. The volume changes and surface morphology of the corroded samples were monitored dynamically using micro-CT over a 16-week period in vivo. Comparison of results between the two sets of samples presented that the corrosion of the microarc fluoridated samples was much slower than that of the untreated ones. The MAF coating was shown to be effective in controlling the corrosion rate and progression of the magnesium alloy.
ISSN:0161-0457
1932-8745
DOI:10.1155/2021/5530788