Effect of Silane-Containing Universal Adhesives on the Bonding Strength of Lithium Disilicate

The purpose of this study was to investigate the effect of silane-containing universal adhesives on the bonding strength of lithium disilicate. Two-hundred-and-forty lithium disilicate blocks were divided into 16 groups according to the following surface treatments: hydrofluoric acid (HF)-treated or...

Full description

Saved in:
Bibliographic Details
Published in:Materials 2021-07, Vol.14 (14), p.3976
Main Authors: Kim, Yu-Ri, Kim, Jae-Hoon, Son, Sung-Ae, Park, Jeong-Kil
Format: Article
Language:English
Subjects:
Adhesives
Bond strength
Bonding strength
Cement
Ceramic bonding
Ceramics
Chemical bonds
Composite materials
Curing
Distilled water
Etching
Failure analysis
Failure modes
Hydrofluoric acid
Interfaces
Lithium
Manufacturing
Resins
Silanes
Surface treatment
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The purpose of this study was to investigate the effect of silane-containing universal adhesives on the bonding strength of lithium disilicate. Two-hundred-and-forty lithium disilicate blocks were divided into 16 groups according to the following surface treatments: hydrofluoric acid (HF)-treated or not, silane-treated or not, and the type of universal adhesive used (All-Bond Universal (ABU); Prime & bond (PB); Clearfil Universal Bond (CU); Single bond Universal (SBU)). After surface treatment, resin discs were bonded to each lithium disilicate using dual-cure resin cement. Bonded specimens were stored in distilled water for 24 h and then subjected to microtensile bond strength (μTBS) test. Failure modes were examined under stereomicroscope. Microscopic observation of bonded interfaces was analyzed using scanning electron microscopy. The μTBS data were statistically analyzed. Regardless of silane treatment, all groups treated with HF showed higher bonding strengths compared to those that were not treated with HF (p < 0.05). In groups treated with HF, the bonding strength increased after silane application (p < 0.05) except PB and CU (p > 0.05). Adhesive failures were dominant in all groups, but some mixed failures were observed in ABU treated with HF and silane. While most of the specimens that were not treated with silane after HF application only showed loose bonding between the ceramic and resin cement due to partial gaps, the specimens treated with silane application after HF showed a tight ceramic–resin interface. In conclusion, the silane in universal adhesives did not effectively improve the bonding strength between lithium disilicate and resin cement.
ISSN:1996-1944
1996-1944
DOI:10.3390/ma14143976