Monomer Conversion, Dimensional Stability, Biaxial Flexural Strength, Ion Release, and Cytotoxicity of Resin-Modified Glass Ionomer Cements Containing Methacrylate-Functionalized Polyacids and Spherical Pre-Reacted Glass Fillers

The aim of this study was to prepare RMGICs for pulp protection that contain polyacids functionalized with methacrylate groups (CMs) to enable light-activated polymerization without the need for toxic 2-hydroxyethyl methacrylate (HEMA) monomers. The effects of using CM liquids with 0 or 5 wt% HEMA o...

Full description

Saved in:
Bibliographic Details
Published in:Polymers 2021-08, Vol.13 (16), p.2742
Main Authors: Potiprapanpong, Wisitsin, Thepveera, Whithipa, Khamsuk, Chutikarn, Channasanon, Somruethai, Tanodekaew, Siriporn, Patntirapong, Somying, Monmaturapoj, Naruporn, Panpisut, Piyaphong
Format: Article
Language:English
Subjects:
Acids
Calcium ions
Conversion
Curing
Cytotoxicity
Dentin
Dimensional changes
Dimensional stability
Fillers
Flexural strength
Fluorides
Glass ionomer cements
Hypotheses
Mechanical properties
Monomers
Polyacids
Polyhydroxyethyl methacrylate
Polymerization
Polymers
Toxicity
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The aim of this study was to prepare RMGICs for pulp protection that contain polyacids functionalized with methacrylate groups (CMs) to enable light-activated polymerization without the need for toxic 2-hydroxyethyl methacrylate (HEMA) monomers. The effects of using CM liquids with 0 or 5 wt% HEMA on the physical/mechanical properties and cytotoxicity of the experimental RMGICs were assessed. Spherical pre-reacted glass fillers (SPG) were used as the powder phase. The experimental RMGICs were prepared by mixing SPG with CM liquid (0 wt% HEMA, F1) or CMH liquid (5 wt% HEMA, F2). Commercial materials (Vitrebond, VB; TheraCal LC, TC) were used for the comparisons. The degree of monomer conversion and fluoride release of both F1 and F2 were significantly lower than those of VB. F1 showed comparable biaxial flexural strength with VB but higher strength than TC. The dimensional stability (mass/volume changes) of the experimental materials was comparable with that of the commercial materials. F1 and F2 exhibited higher Sr/Ca ion release and relative cell viability than VB. The use of CMH liquid reduced the strength but enhanced the fluoride release of the experimental RMGICs. In conclusion, the experimental RMGICs showed comparable strength but lower cytotoxicity compared to the commercial RMGICs. These novel materials could be used as alternative materials for pulp protection.
ISSN:2073-4360
2073-4360
DOI:10.3390/polym13162742