Different Preparation Method of Nanocellulose from Macaranga gigantea and Its Preliminary Study on Packaging Film Potential

• Published in: Polymers 2022-10, Vol.14 (21), p.4591
• Main Authors: Jasmani, Latifah, Jamaluddin, Nurul Ain Nadirah, Rusli, Rafeadah, Adnan, Sharmiza, Zakaria, Sarani
• Format: Article
• Language: English
• Subjects: Analytical chemistry; Biodegradability; Caustic soda; Cellulase; Cellulose; Conversion; Enzymes; Fourier transforms; Hydrochloric acid; Infrared analysis; Infrared spectroscopy; Landfill; Lignin; Nanomaterials; Packaging; Radiation; Raw materials; Sodium; Spectrum analysis; Sulfuric acid; Tensile tests; Thermal stability; Thermogravimetric analysis; Thin films; Ultrafines; Water vapor; X-ray diffraction
• ISSN: 2073-4360; 2073-4360
• DOI: 10.3390/polym14214591

Nanocellulose is a versatile cellulosic nanomaterial that can be used in many application areas. Applying different preparation strategies leads to different types of nanocellulose. In this study, nanocrystalline cellulose (NCC) and nanofibrillated cellulose (NFC) were prepared from lesser known wood species, viz., , using sulfuric acid hydrolysis and enzymatic pretreatment with ultrafine grinding approaches, respectively. The respective nanocellulose was characterized by means of Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) analysis, thermogravimetric analysis (TGA), atomic force microscopy (AFM). It was then converted into a thin film to assess its performance which includes tensile test, transparency, air permeance, water vapor transmission rate (WVTR), and water vapor permeability (WVP) properties. NCC and NFC produced from the raw material of Macaranga had average widths of 6.38 ± 3.92 nm and 13.17 ± 12.71 nm, respectively. Peaks in FTIR spectra showed the conversion of Macaranga wood to nanocellulose by the presence of cellulose fingerprint as well as absence of lignin and hemicellulose after alkaline treatment. The successful conversion was also supported by XRD analysis which displayed the increased crystallinity value from 54% to 70%. TGA decomposition pattern at 200-490 °C revealed the thermal stability of the samples. The thin film produced from nanocelluloses had WVTR values of 4.58 and 12.14 g/(day·m ) for NFC and NCC, respectively, comparable to those of films from polyester and oriented polypropylene. Nanocellulose-based thin film has the potential to be used as sustainable and biodegradable packaging.