Effect of Rotary Swaging on the Structure, Mechanical Characteristics and Aging Behavior of Cu-0.5%Cr-0.08%Zr Alloy
A study of the effect of rotary swaging (RS) on the microstructure and properties of the pre-extruded and pre-quenched Cu-0.5%Cr-0.08%Zr alloy was performed. RS leads to the formation of an ultrafine-grained (UFG) microstructure. UFG structure formation caused by RS increases the ultimate tensile st...
Saved in:
Published in: | Materials 2022-12, Vol.16 (1), p.105 |
---|---|
Main Authors: | , , , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | A study of the effect of rotary swaging (RS) on the microstructure and properties of the pre-extruded and pre-quenched Cu-0.5%Cr-0.08%Zr alloy was performed. RS leads to the formation of an ultrafine-grained (UFG) microstructure. UFG structure formation caused by RS increases the ultimate tensile strength (UTS) up to 443 ± 5 MPa and 597 ± 9 MPa for pre-quenched and pre-extruded alloys, respectively. Additionally, the reduction in ductility occurs after RS. It should be noted that UTS is increased for a pre-quenched alloy, while the strength of a pre-extruded alloy is dropped. The growth of UTS for the pre-quenched alloy is associated with the precipitation of fine Cr particles, whereas the recovery processes in the pre-extruded alloy induce the reduction in its UTS. An additional advantage of RS is an increase in the fatigue limit of the pre-quenched alloy up to 265 MPa, and of the pre-extruded alloy up to 345 MPa. The combination of extrusion and RS allows for the increase of the UTS of the Cu-0.5%Cr-0.08%Zr alloy up to 597 ± 9 MPa, while the levels of ductility and electrical conductivity are 10.9 ± 0.9% and 82.0 ± 1.7% IACS, respectively. |
---|---|
ISSN: | 1996-1944 1996-1944 |
DOI: | 10.3390/ma16010105 |