Hydrodeoxygenation of bio-oil using different mesoporous supports of NiMo catalysts

• Main Authors: Rinaldi, Nino, Simanungkalit, Sabar P., Kristiani, Anis
• Format: Conference Proceeding
• Language: English
• Subjects: Aluminum oxide; Biomass energy production; Catalysis; Catalysts; Catalytic activity; Chemical properties; Deoxygenation; Fourier transforms; Molybdenum; Nickel; Organic chemistry; Oxygen content; Physical properties; Surface area; Titanium dioxide; X-ray diffraction
• ISSN: 0094-243X; 1551-7616
• DOI: 10.1063/1.5011935

Biomass as a renewable and sustainable resources need to utilize in many applications, especially for energy application. One of its energy application is about converting biomass into bio-oil. High oxygen content in bio-oil needs to be upgraded through hydrodeoxygenation process before being used as transportation fuel. The development of heterogenenous catalysts become an important aspect in hydrodeoxygenation process, in particular the upgrading process of bio−oil. Several supporting mesoporous materials, such as TiO2, Al2O3 and MCM−41 have unique properties, both physical and chemical properties that can be utilized in various application, including catalyst. These heterogeneous catalysts were modified their catalytic properties by impregnation with some transition metal. The effect of various supporting material and transition metal impregnated were also studied. Their chemical and physical properties were characterized by X-Ray Diffraction, X-Ray Fluororesence, Fourier Transform Infra-Red, and Surface Area Analyzer. The result of characterizations showed that Ni-Mo/TiO2 is more crystalline than Ni-Mo/MCM-41 and Ni-Mo/Al2O3. In other hand, the specific surface area of Ni-Mo/TiO2 is lower than others. These heterogeneous catalysts were tested their catalytic activity in upgrading bio-oil. The liquid products produced were analyzed by using Elemental Analyzer. The result of catalytic activity tests showed catalysts resulted Ni-Mo/TiO2 exhibits best catalytic activity in hydrodeoxygenation process. The oxygen content decreased significantly from 41.61% to 26.22% by using Ni-Mo/TiO2. Compared with Ni-Mo/TiO2, Ni−Mo/MCM-41 and Ni-Mo/Al2O3 decrease lower to 33.22% % and 28.34%, respectively. Ni-Mo/TiO2 also resulted the highest Deoxygenation Degree (DOD) as of 55% compared with Ni-Mo/MCM-41 and Ni-Mo/Al2O3 as of 31.99 % and 47.99%, respectively.