Low-temperature CO oxidation over CuO-CeO2/SiO2 catalysts:Effect of CeO2 content and carrier porosity
The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 adsorption/desorption at low temperature,X-ray diffraction (XRD),temperature-programm...
Saved in:
Published in: | Journal of natural gas chemistry 2010-07, Vol.19 (4), p.355-361 |
---|---|
Main Authors: | , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 adsorption/desorption at low temperature,X-ray diffraction (XRD),temperature-programmed reduction by H2 (H2-TPR),oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS).The results suggested that,the ceria content and the porosity of SiO2 carrier possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts.When appropriate content of CeO2 (Ce content 8 wt%) was added,the catalytic activity was greatly enhanced.In the catalyst supported on silica carrier with larger pore diameter,higher dispersion of CuO was observed,better agglomeration-resistant capacity was displayed and more lattice oxygen could be found,thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation. |
---|---|