Preparation of Styrene-acrylate Latex Used in Ultra-low VOC Building Internal Wall Coating

Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core m...

Full description

Saved in:
Bibliographic Details
Published in:Journal of Wuhan University of Technology. Materials science edition 2008-02, Vol.23 (1), p.65-70
Main Author: 陈立军 WU Fengqin ZHUANG Xinyu YANG Jian LI Rongxian
Format: Article
Language:English
Subjects:
内墙涂料
建筑物
易挥发有机化合物
苯乙烯-丙烯酸脂胶乳漆
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core monomer to shell monomer was approximately 1.35. It is found that many factors such as emulsifiers, initiators, reaction temperature, pH value and polymerization technology have influences on the permormance of styrene-acrylate latex. The prepared latex was characterized by TEM and FTIR. The obtained latex with T of 20.57 ℃, MFT or5.0 ℃, and good stability, had good stability of film forming.
ISSN:1000-2413
1993-0437
DOI:10.1007/s11595-006-1065-2