Tensile and fracture behavior of DZ951 Ni-base superalloy

The tensile and fracture behavior of DZ951 directionally solidified Niobase superalloy was studied in the temperature range of 20-1 100 ℃. The fracture mode was examined by scanning electron microscopy. The results show the experimental temperature has no significant effect on the tensile strengths,...

Full description

Saved in:
Bibliographic Details
Published in:Transactions of Nonferrous Metals Society of China 2006-12, Vol.16 (A03), p.1949-1952
Main Author: 储昭贶 于金江 孙晓峰 赵乃仁 管恒荣 胡壮麒
Format: Article
Language:English
Subjects:
高温合金
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The tensile and fracture behavior of DZ951 directionally solidified Niobase superalloy was studied in the temperature range of 20-1 100 ℃. The fracture mode was examined by scanning electron microscopy. The results show the experimental temperature has no significant effect on the tensile strengths, which are greater than 1 000 MPa from room temperature to 800 ℃. The yield strength reaches its maximum （970 MPa） at 800 ℃. When the experimental temperature is higher than 800 ℃, the tensile and yield strengths decrease evidently and the ductility increases remarkably. The fractograph of fracture surface for the tensile specimen at room temperature shows a dimple-ductile fracture mode. The fractograph from 600 to 800 ℃ shows a slide fracture mode. The fractograph from 900 to 1 100 ℃ exhibits a creep rupture mode with uneven deformation.
ISSN:1003-6326