Portevin-Le Chatelier effect in Al-Zn-Mg-Cu-Zr aluminum alloy
Portevin-Le Chatelier (PLC) effect in a severely cold-rolled Al-Zn-Mg-Cu-Zr aluminum alloy (AA7055 type) plate before and after annealing was investigated. The results show that the sample annealed at 300 °C undergoes PLC effect, whereas the PLC effect is not observed in the deformed sample or the s...
Saved in:
Published in: | Transactions of Nonferrous Metals Society of China 2009-10, Vol.19 (5), p.1071-1075 |
---|---|
Main Authors: | , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Portevin-Le Chatelier (PLC) effect in a severely cold-rolled Al-Zn-Mg-Cu-Zr aluminum alloy (AA7055 type) plate before and after annealing was investigated. The results show that the sample annealed at 300 °C undergoes PLC effect, whereas the PLC effect is not observed in the deformed sample or the samples annealed at 110 °C or 200 °C. The main precipitates in the sample annealed at 300 °C are the coarsened η phases, while a mixture of small η' phases and η phases dominates in the sample annealed at 200 °C. In the deformed sample and sample annealed at 110 °C, GP zone are the main precipitates. The different flow behaviors are ascribed to the type of precipitates as well as the dislocation density differences. |
---|---|
ISSN: | 1003-6326 |
DOI: | 10.1016/S1003-6326(08)60408-2 |