Fracture mechanisms of additively manufactured polylactide: Effect of in vitro hydrolytic degradation

This is the first study considering the effect of in vitro hydrolytic degradation at 37 °C on fracture mechanism of the most important aspect of additive manufacturing – the interface between layers. Specimens were tested transversely (failure between layers) and longitudinally (failure directly thr...