Activity and hydrothermal stability of CeO_2–ZrO_2–WO_3 for the selective catalytic reduction of NO_x with NH_3

• Published in: 环境科学学报：英文版 2016 (4), p.168-177
• Main Author: Zhongxian Song Ping Ning Qiulin Zhang Hao Li Jinhui Zhang Yancai Wang Xin Liu Zhenzhen Huang
• Format: Article
• Language: English
• Subjects: CeO2; ZrO2; 催化活性; 氧化还原性能; 水热稳定性; 水热老化; 老化温度; 选择性催化还原
• ISSN: 1001-0742; 1878-7320

A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃.The effect of hydrothermal treatment of CZW catalysts on SCR activity was investigated in the presence of 10% H2O.The fresh catalyst showed above 90% NOx conversion at 201–459℃,which is applicable to diesel exhaust NOx purification（200–440℃）.The SCR activity results indicated that hydrothermal aging decreased the SCR activity of CZW at low temperatures（below 300℃）,while the activity was notably enhanced at high temperature（above 450℃）.The aged CZW catalyst（hydrothermal aging at 700℃ for 8 hr）showed almost 80% NOx conversion at 229–550℃,while the V2O5–WO3/TiO2 catalyst presented above 80% NOx conversion at 308–370℃.The effect of structural changes,acidity,and redox properties of CZW on the SCR activity was investigated.The results indicated that the excellent hydrothermal stability of CZW was mainly due to the CeO2–ZrO2 solid solution,amorphous WO3 phase and optimal acidity.In addition,the formation of WO3 clusters increased in size as the hydrothermal aging temperature increased,resulting in the collapse of structure,which could further affect the acidity and redox properties.