Magnesium sulfate attack on portland cement paste-I. Microstructural analysis

• Published in: Cement and concrete research 1992, Vol.22 (1), p.169-180
• Main Authors: Bonen, David, Cohen, Menashi D.
• Format: Article
• Language: English
• Subjects: Applied sciences; Buildings. Public works; Cement concrete constituents; Cements; Exact sciences and technology; Materials; Properties and test methods; Properties of anhydrous and hydrated cement, test methods
• ISSN: 0008-8846; 1873-3948
• DOI: 10.1016/0008-8846(92)90147-N

The mechanism of magnesium sulfate attack in portland cement and portland cement with silica fume paste was studied by investigating the microstructure and composition of specimens immersed for one year in magnesium sulfate solution. Results are presented in two parts. Part I, presents the microstructure of the pastes. Part II, presents the chemical and mineralogical variations across the specimen together with a proposed mechanism of magnesium sulfate attack. The magnesium sulfate attack resulted in the formation of the “surface double-layer” which was composed of brucite and gypsum layers. In addition, there was a sequential formation of inner gypsum layers resembling the occurence of lisegang bands found in rocks. The surface double-layer was composed of brucite, about 40 to 120 μm thick, and followed by a contiguous layer of gypsum, about 20 to 70 μm thick. Subsequently, up to four internal gypsum layers were deposited at depths of up to 1200 μm from the surface. These layers were parallel to the beam surfaces ranging in thicknesses from 15 to 60 μm. In portland cement with silica fume paste there were almost no inner gypsum layers, instead, massive deposition of dispersed gypsum crystals appeared up to at a distance of about 800 μm from the surface. The attack had apparently influenced the local degree of hydration of the cement constituents; near the surface only residual ferrite and belite crystals were observed, but in the middle, unreacted alite and belite were predominant.