Enhancing released electrical energy density of poly(vinylidene fluoride-co-trifluoroethylene)-graft-poly(methyl methacrylate) via the pre-irradiation method

• Published in: Applied surface science 2019-01, Vol.465, p.643-655
• Main Authors: Chu, Huiying, Fu, Chao, Wu, Xianyou, Tan, Zhongyang, Qian, Jing, Li, Weiyan, Ran, Xianghai, Nie, Wei
• Format: Article
• Language: English
• Subjects: Enhanced released energy density; Ferroelectric polymer; Nanoconfinement effect; P(VDF-TrFE)-g-PMMA; Pre-irradiation grafting method
• ISSN: 0169-4332; 1873-5584
• DOI: 10.1016/j.apsusc.2018.08.222

•P(VDF-TrFE)-g-PMMAs had been successfully synthesized via pre-irradiation grafting method.•Grafted-PMMA was beneficial for the formation of smaller ferroelectric domains.•The best performance of Ue,released was 77% higher than pristine P(VDF-TrFE). Poly(vinylidene fluoride) (PVDF)-based ferroelectric polymers with excellent flexibility and tuneable ferroelectric performance characteristics have attracted continuous attention for high energy storage applications. To produce ideal novel ferroelectric polymers to enhance released energy density and reduced hysteresis loss, smaller ferroelectric domains are necessary. In this study, we prepared poly(vinylidene fluoride-co-trifluoroethylene)-graft-poly(methyl methacrylate) (P(VDF-TrFE)-g-PMMA) graft copolymers via the pre-irradiation process, achieving the transition from normal ferroelectric performance to either antiferroelectric-like or linear behaviour. Compared to the atom transfer radical polymerization (ATRP), this method is attractive due to its unique merits, such as user-friendly control, short processing time and catalyst-free reaction. By using the nanoconfinement effect concept, grafted-PMMA with fairly strong intermolecular interactions was miscible with P(VDF-TrFE) in an amorphous phase, which effectively impeded the formation of large lamellar crystals. Compared to pristine film, the best performance was achieved for the irradiated grafting film with dielectric loss reduced by 67% (from 0.27 to 0.09) at 1 MHz, released energy density increased by 77% (from 2.2 to 9.5 J/cm3) and released energy efficiency improved by 80% (from 0.15 to 0.75 J/cm3). This work provides a simple and efficient strategy for the fabrication of novel dielectrics for high released energy density and low loss application.