Intermediate tin oxide in stable core-shell structures by room temperature oxidation of cluster-assembled nanostructured Sn films
[Display omitted] •Nanostructured Sn films are deposited by Supersonic Cluster Beam Deposition in high vacuum conditions.•Room temperature air exposure generates stable core-shell structures, shell measuring about 4 nm.•Core is tetragonal metallic β-tin, shell is tin oxide with similar quantity of S...
Saved in:
Published in: | Applied surface science 2024-06, Vol.658, p.159846, Article 159846 |
---|---|
Main Authors: | , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | [Display omitted]
•Nanostructured Sn films are deposited by Supersonic Cluster Beam Deposition in high vacuum conditions.•Room temperature air exposure generates stable core-shell structures, shell measuring about 4 nm.•Core is tetragonal metallic β-tin, shell is tin oxide with similar quantity of Sn oxidation states Sn2+ and Sn4+.•Raman signature of Sn3O4 is observed, demonstrating spontaneous formation of this intermediate oxide at room temperature.•The oxidation gradient Sn-SnO-Sn3O4-SnO2 is proposed for core-shell system.
Room temperature oxidation of cluster-assembled nanostructured Sn films obtained by supersonic cluster beam deposition was investigated. Sn clusters smaller than about 10 nm are observed to be fully oxidized while in larger ones, as well as in Sn islands formed by clusters coalescence, completion of Cabrera-Mott process is prevented resulting in partial oxidation. Core-shell structures are therefore obtained, with shell thickness of about 4 nm. Core is composed by highly ordered, tetragonal β-tin, with micro-strain of 0.16 %, while shell is composed of tin oxides, where similar quantity of both Sn oxidation states Sn2+ and Sn4+ are observed, according to XPS. The presence in the samples of metallic tin, SnO, and SnO2 is confirmed by valence band photoelectron spectrum, whose components show edges at 0, 0.6, and 3.2 eV from Fermi level, respectively. Raman spectroscopy highlights the presence of Sn3O4 (short version of Sn2+2O2Sn4+O2), which confirms the spontaneous formation of this intermediate oxide. It is therefore proposed that an oxidation gradient Sn-SnO-Sn3O4-SnO2 characterizes core-shell system resulting from room temperature Cabrera-Mott oxidation of cluster-assembled nanostructured films. |
---|---|
ISSN: | 0169-4332 1873-5584 |
DOI: | 10.1016/j.apsusc.2024.159846 |