Continuum damage mechanics combined with the extended finite element method for the total life prediction of a metallic component
Fatigue is a major reason for the failure of components subjected to cyclic loadings, and the fatigue failure of components can be divided into two phases: crack initiation and crack propagation. In this study, continuum damage mechanics (CDM) combined with the extended finite element method (XFEM)...
Saved in:
Published in: | International journal of mechanical sciences 2017-05, Vol.124-125, p.48-58 |
---|---|
Main Authors: | , , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Fatigue is a major reason for the failure of components subjected to cyclic loadings, and the fatigue failure of components can be divided into two phases: crack initiation and crack propagation. In this study, continuum damage mechanics (CDM) combined with the extended finite element method (XFEM) is proposed to predict the total fatigue life of components, that is, the crack initiation life and propagation life. First, the damage-coupled elastic-plastic constitutive equations and fatigue damage evolution equations are derived to calculate the fatigue damage and to predict the crack initiation life of a material under cyclic loads. Second, according to the distribution of the damage field and trend of fatigue damage evolution, the criterion to judge the formation of crack initiation is proposed. Third, based on linear elastic fracture mechanics (LEFM) with XFEM, the crack propagation life is predicted. Then, fatigue crack initiation and propagation analysis for a specimen with a preset pit and for a fuselage structure with opening are conducted using the method described above. Finally, fatigue experiments are conducted to verify the proposed method, and the predicted total fatigue life and crack propagation path are in accordance with the experimental results.
•A new method to calculate the total fatigue life of a component is proposed.•Fatigue damage evolution model for crack initiation analysis is established.•The criterion to judge the formation of crack initiation is proposed.•The calculated results agree well with the experimental results. |
---|---|
ISSN: | 0020-7403 1879-2162 |
DOI: | 10.1016/j.ijmecsci.2017.03.002 |