Understanding the mechanisms behind ultrasonic vibration in resistance spot welding of aluminum and steel

An ultrasonic-assisted resistance spot welding process, which can improve the quality of aluminum/steel spot-welded joints, has been developed. However, the mechanism of the thermal-electrical-mechanical behavior caused by the ultrasonic longitudinal vibration to welding process has not been clarifi...

Full description

Saved in:
Bibliographic Details
Published in:Journal of materials processing technology 2024-08, Vol.329, p.118442, Article 118442
Main Authors: Ren, Baokai, Zhou, Kang, Wang, Gang, Yu, Wenxiao, Ivanov, Mikhail
Format: Article
Language:English
Subjects:
Aluminum/steel
Double-nugget evolution
Finite element
Impact mechanism
Resistance spot welding
Ultrasonic longitudinal vibration
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:An ultrasonic-assisted resistance spot welding process, which can improve the quality of aluminum/steel spot-welded joints, has been developed. However, the mechanism of the thermal-electrical-mechanical behavior caused by the ultrasonic longitudinal vibration to welding process has not been clarified. In this study, the role and impact mechanisms of ultrasonic longitudinal vibration during the welding process to form joints were confirmed by combining the microstructural characterization of the formed joints with the signal analysis of the process, as well as the analysis of the independent finite element numerical calculation results. Additionally, the interface metallurgical reaction behavior, welding defects, fracture behavior, and joint strength characteristics of ultrasonic-assisted aluminum/steel resistance spot welding joints were comprehensively analyzed, and the results indicated that the sizes of the aluminum/steel nuggets decreased. It could be attributed to the competition among multiple ultrasonic effects. Specifically, ultrasonic vibration decreased the contact resistance between the aluminum/steel sheets, whereas the acoustic cavitation and acoustic streaming effects increased the electrical conductivity of molten steel and thermal conductivity of molten aluminum, respectively. Moreover, ultrasonic vibration promoted the radial creep of molten and near-molten aluminum, which expanded in the effective bonding area between the two workpieces. Furthermore, ultrasonic vibration effectively reduced the thickness of the intermetallic compound layer (
ISSN:0924-0136
DOI:10.1016/j.jmatprotec.2024.118442