Preparation of geopolymers from thermally activated lithium slag: Activity enhancement and microstructure

As an industrial by-product of the lithium extraction process from spodumene, lithium slag (LS) is less reactive, rendering it a chemically infeasible binder. In this study, a thermal activation approach was employed to enhance the reactivity of LS. The underlying mechanisms of LS's thermal act...

Full description

Saved in:
Bibliographic Details
Published in:Journal of Building Engineering 2024-07, Vol.88, p.109256, Article 109256
Main Authors: Luo, Xiaofeng, Huang, Liang, Yan, Libo, Li, Yin, Wei, Linggang, Chen, Zhijun, Qu, Yiqun
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:As an industrial by-product of the lithium extraction process from spodumene, lithium slag (LS) is less reactive, rendering it a chemically infeasible binder. In this study, a thermal activation approach was employed to enhance the reactivity of LS. The underlying mechanisms of LS's thermal activation at various temperatures were thoroughly explored through XRD and ICP. The results indicated that alterations in the aluminosilicate composition of LS occurred during calcination between 500 °C and 900 °C, leading to the transformation of spodumene into amorphous forms. Particularly noteworthy was the initial increase in the LS amorphous phase content with increasing temperature, followed by a subsequent decline. Building upon these findings, a lithium slag geopolymer (LSG) was prepared via alkali activation, using the activated LS as the exclusive precursor. It was observed that elevating the content of active components in LS enhanced the geopolymerization reactions, resulting in an improved mechanical strength of LSG. Remarkably, after 28 days of aging, geopolymer specimens prepared from LS calcined at 700 °C exhibited a compressive strength of 36.0 MPa. Combining these results with FTIR and SEM-EDS analyses, it becomes evident that suitable calcination temperatures empower LS to release a higher quantity of silicon and aluminum ions. These ions play a significant role in the geopolymerization process, leading to the formation of an amorphous sodium (calcium) aluminosilicate hydrate (N(C)-A-S-H) gel. This gel acts as a binder, tightly binding the residual solid particles, and thus forming a denser microstructure. •Calcination alters the phase composition and crystal structure of lithium slag.•Calcination promotes the dissolution of Si and Al ions in lithium slag.•Geopolymers were prepared using activated lithium slag as the sole precursor.
ISSN:2352-7102
2352-7102
DOI:10.1016/j.jobe.2024.109256