Evolution of microstructure and mechanical properties of aluminum matrix composites reinforced with dual-phase heterostructures

• Published in: Materials science & engineering. A, Structural materials : properties, microstructure and processing Structural materials : properties, microstructure and processing, 2024-05, Vol.901, p.146500, Article 146500
• Main Authors: Su, W.X., Wang, H.M., Li, G.R., Zhang, Y.F.
• Format: Article
• Language: English
• Subjects: Aluminum matrix composite; High entropy alloys; Hybrid reinforcement; Microstructure
• ISSN: 0921-5093; 1873-4936
• DOI: 10.1016/j.msea.2024.146500

The trade-off between strength and plasticity has long been challenging in particle-reinforced aluminum matrix composites (PRAMCs). This study proposes an innovative approach for preparing aluminum matrix composites (AMCs) using a dual-phase hybrid of FeCoNiCrMn high entropy alloy (HEA) and multiscale aluminum oxide (Al2O3) particles. The microstructure evolution and strengthening mechanisms were evaluated through scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). The results demonstrated that the dual-phase particle strengthening resulted from the alternating distribution and synergistic action of HEA and Al2O3 particles within the matrix, forming a continuous strain buffer with a strength gradient. Notably, introducing HEA and nano-Al2O3 led to a higher density of dislocations. Additionally, EBSD analysis revealed a uniform strain distribution within the AMCs, with a significant concentration of kernel average misorientation (KAM) near the grain boundaries (GBs). In terms of micromechanical properties, the micro-zones of heterogeneous phases exhibit exceptionally high elastic modulus and nanohardness. In terms of macroscopic mechanical properties, the material exhibited impressive ultimate compressive strength and compression ratio values of 447.9 MPa and 37.9 %, respectively. These results represented a remarkable enhancement of 72.1 % and 6.6 % compared to the single FeCoNiCrMn HEA strengthening. Moreover, when applying the HEA + nano-Al2O3 blending mode, the ultimate compressive strength further increased to 506.7 MPa, representing an astonishing boost of 94.7 %. This significant strength improvement can be attributed to effective interfacial bonding, grain refinement, and a high dislocation density resulting from both HEA and Al2O3 particles. A novel method for fabricating aluminum matrix composites (AMCs) utilizing a dual-phase hybrid of FeCoNiCrMn high-entropy alloy (HEA) and multiscale Al2O3 particles was investigated. The interfacial microstructural evolution and strengthening mechanisms were analyzed through scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron backscatter diffraction (EBSD), and other techniques. The results revealed that the HEA and Al2O3 particles were evenly distributed throughout the aluminum matrix. The mixing of HEA and nano-sized Al2O3 induced higher lattice distortion and increased dislocation density. The grain orientat