Phase equilibria, martensitic transformations and deformation behaviors of the subsystem of Cantor alloy−low-cost Fe-Mn-Cr alloys

Investigations of the Fe-Mn-Cr system are not only significant for developing Cantor alloy but also valuable for designing low-cost, high-strength steel. In this study, we experimentally determined the phase equilibria of this system for establishing the thermodynamic database. Additionally, the inf...

Full description

Saved in:
Bibliographic Details
Published in:Materialia 2021-12, Vol.20, p.101231, Article 101231
Main Authors: Ruan, Jingjing, Ueshima, Nobufumi, Li, Haoge, Oikawa, Katsunari
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Investigations of the Fe-Mn-Cr system are not only significant for developing Cantor alloy but also valuable for designing low-cost, high-strength steel. In this study, we experimentally determined the phase equilibria of this system for establishing the thermodynamic database. Additionally, the influences of Mn on both the phase transformation and deformation behaviors of the Fe-Mn-Cr alloys were studied. Fe was found to solute into σHT phase with a large solubility at 1323 and 1473 K. A (βMn) single-phase region was initially discovered at 1473 K. The (βMn)+(γFe) and σHT+(Cr) two-phase regions were respectively found to be very narrow. During tensile testing, the transformation-induced-plasticity (TRIP)- type was discovered to change from ε→α′ to (γFe)→ε when Mn increased from 20 to 30 at. %. The stacking fault energy (SFE) was measured to be 8.1 mJ·m−2 for 30Mn alloy. Contrarily, the stacking fault did not seem to occur during the tensile testing of 40Mn alloy. The 0.2 % proof stresses for Fe(90-x)MnxCr10 alloys were measured to be 633 (10Mn), 345 (20Mn), 166 (30Mn), and 188 MPa (40Mn), respectively. The TRIP effect was discovered in the tensile testing of 30Mn alloy, which exhibited an ultimate tensile strength of 755 MPa and a uniform elongation of 38.7 %. It is to be noted that no recovery of work-hardening rate occurred during the tensile testing of 40Mn alloy. The investigated phase equilibria and deformation behaviors of the Fe-Mn-Cr alloys are believed to accelerate the design of Cantor-alloy-related materials and Fe-Mn-Cr-based high-strength steel. Determined Fe-Mn-Cr ternary systems: (a) 1323 K, (b) 1473 K. (c) Tensile ture strain-stress curves and corresponding work-hardening rate curves for 10Mn, 20Mn, 30Mn and 40 Mn alloys. (d) The XRD results of the fractured 20Mn, 30Mn and 40 Mn alloys. (e)-(f) Phase maps of the 20Mn and 30Mn alloys after tensile test [Display omitted]
ISSN:2589-1529
2589-1529
DOI:10.1016/j.mtla.2021.101231