Synthesis and structural analysis of calcined poultry manure for hydroxyapatite development

This study investigates the viability of utilizing poultry manure, an abundant and low-cost waste material, for the synthesis of hydroxyapatite (HAp), a critical biomaterial for bone regeneration. Calcination of poultry manure was conducted at 750°C, 800°C, and 850°C for 5 h to produce HAp. The proc...

Full description

Saved in:
Bibliographic Details
Published in:Next Sustainability 2025, Vol.5, p.100079, Article 100079
Main Authors: Alaneme, Kenneth Kanayo, Oke, Samuel Ranti, Fagbayi, Sandra Boluwatife, Alabi, Oladunni O., Ojo, Ochuko Mary, Kareem, Sodiq Abiodun, Folorunso, Davies O.
Format: Article
Language:English
Subjects:
Biomaterial
Bone implant
Calcination
Characterization
Hydroxyapatite
Poultry manure
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This study investigates the viability of utilizing poultry manure, an abundant and low-cost waste material, for the synthesis of hydroxyapatite (HAp), a critical biomaterial for bone regeneration. Calcination of poultry manure was conducted at 750°C, 800°C, and 850°C for 5 h to produce HAp. The processed poultry manure was then characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) with energy dispersive X-ray spectrometry (EDS), X-ray fluorescence (XRF), and X-ray diffraction (XRD) analyses. The FTIR analysis confirmed the formation of HAp through characteristic phosphate absorption bands, with the highest purity observed at 850°C. SEM analysis revealed that increasing calcination temperature enhanced the crystallinity and particle uniformity of the samples. XRF analysis showed a significant increase in CaO (40.229–43.328 %) and P2O5 (17.905–19.239 %) content with rising temperatures, crucial for HAp synthesis. The Ca/P ratios were determined to be 1.28, 1.54, and 1.71, respectively, indicating variations in purity and phase composition. The 800°C provides a near-ideal Ca/P ratio while the 850°C achieves a ratio slightly above the ideal, indicating a high-purity HAp phase. XRD analysis corroborated these findings, identifying hydroxyapatite (Ca10P6O26H2), as the predominant phase with minimal secondary phases. These results suggest that calcination at 850°C is optimal for producing high-purity HAp from poultry manure, offering a sustainable and cost-effective alternative to synthetic HAp production for biomedical applications.
ISSN:2949-8236
2949-8236
DOI:10.1016/j.nxsust.2024.100079