Tribological performance under abrasive wear of Fe-Cr-C+Nb coating deposited by FCAW process

• Published in: Wear 2023-06, Vol.523, p.204824, Article 204824
• Main Authors: Sousa, Jurandir Marcos Sá de, Gil, Gilson Silva, Barbosa, Matheus dos Santos, Garcia, Douglas Neves, Lobato, Mauro Quaresma, Machado, Paulo Cordeiro
• Format: Article
• Language: English
• Subjects: CrC and NbC carbides; Dilution; FCAW process; Fe-Cr-C+Nb alloys
• ISSN: 0043-1648; 1873-2577
• DOI: 10.1016/j.wear.2023.204824

This paper aims to investigate the abrasion resistance performance of Iron-Crhomium-Carbon + Niobium (Fe-Cr-C + Nb) coatings deposited by Flux-Cored Arc Welding (FCAW) process. Two coatings conditions were prepared in a 1-layer setup, with a selfshielded tubular wire over SAE 1020 carbon steel substrate, varying the FCAW parameterization levels, searching to reproduce different conditions of welding energy and their respective effects on the coatings' properties. Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) were employed in the microstructure and wear micromechanism analysis. X-ray Energy Dispersive Spectroscopy (EDS) was used for chemical composition assessment and Vickers microdurometer for hardness evaluation. In the tribological attempt, it was used the dry/sand rubber wheel apparatus according to ASTM G65. From the results, in neither sample of the two coating conditions, deleterious defects were observed on the surfaces, as well as in the cross-sections, such as lack of fusion and process interruptions. Dilutions were sufficient to ensure metallurgical bond without compromising layer geometry. Cold cracking characteristics of the process and material were observed, which did not significantly influence the performance of the coatings. The microstructure of both coatings showed CrC and NbC carbides dispersed in the Fe-matrix, whose volume fraction and mean free path between them varied as a function of dilution. The greater Nb-content and less intense heat input in the lower dilution coating provided greater refining of the CrC, NbC, and Fe-matrix strength, which was reflected in higher hardness, lower wear rate, and less severe abrasive wear micromechanism. •Fe-Cr-C + Nb coatings showed resistant metallurgical bond and no geometry defects.•FCAW process must be optimized to keep low dilution and ensure geometric integrity.•The microstructure showed CrC and NbC carbides dispersed in the Fe-matrix.•Larger volume and narrower mean free path between carbides increased the hardness.•Abrasion resistance was governed by the hardness and strengthening of CrC and NbC.