Real-Time Measurement on the Heat Release Property of Titanium Blended with Different Carbon Allotropes, under Externally Constant Heat Flux

• Published in: Metals (Basel ) 2019-09, Vol.9 (9), p.981
• Main Authors: Wang, Yachao, Zhao, Jiangping
• Format: Article
• Language: English
• Subjects: Allotropy; Calcium aluminate; Carbon; Carbon black; Chemical evolution; Combustion; cone calorimeter; Cone calorimeters; Graphite; Gravimetry; Heat; Heat flux; heat release properties; Heat release rate; Heat transfer; Oxidation; Particle size; Propagation; Raw materials; Real time; TG/DSC; thermodynamic calculation; Time measurement; Titanium; Titanium carbide; Titanium dioxide; X-ray diffraction
• ISSN: 2075-4701; 2075-4701
• DOI: 10.3390/met9090981

Ti/C blended powder is commonly employed as an initiating combustion agent for preparing calcium aluminate; a dedicated test system is exploited for real-time examining of the heat release of Ti/C blended powder during combustion under atmosphere conditions with an externally constant heat flux of 973 K, which is comprised of cone calorimeter, thermal-gravimetry/differential scanning calorimetry, X-ray diffraction (XRD), scanning electron microscope/energy dispersive spectrometer, and a theoretical thermal calculation, with the aim of quantitatively illuminating its combustion mechanism in depth. Furthermore, a comparison of the heat release property of titanium powder blended with different carbon allotropes, including natural flaky graphite (FG), carbon black (CB), expandable graphite (EG), and vermicular graphite (VG) is preliminarily investigated, to clarify the effect of different carbon allotropes on the heat release property of Ti/C blended powder. It reveals that the oxidation reaction between Ti and O2 initiates the subsequent combination of TiC through a thermal explosion reaction, using graphite (FG, VG, or EG) and Ti powder as the starting materials, respectively. Moreover, EG facilitates an accelerated (fire growth index of 0.42 kW·m−2·s−1) and enhanced peak heat release rate (pHRR) of 30.7 kW·m−2 at 73 s, while VG suppresses the heat release with the pHRR of 5.2 kW·m−2 at 64 s and fire growth index of 0.08 kW·m−2·s−1, and FG favors the formation of TiC with a higher crystallinity from XRD. Additively, the prior NaOH-impregnation is favorable for the formation of TiC for Ti/CB blended powder, although the TiO2 predominates final combustion production. It reveals the chemical evolution and mechanisms evolved in the formation of TiC during ignition.