The Influence of the ZrO.sub.2 Solid Solution Amount on the Physicochemical Properties of Al.sub.2O.sub.3-ZrO.sub.2-Y.sub.2O.sub.3-CeO.sub.2 Powders

• Published in: Powder metallurgy and metal ceramics 2021-07, Vol.60 (3-4), p.129
• Main Authors: Smyrnova-Zamkova, M.Yu, Ruban, O.K, Bykov, O.I, Holovchuk, M.Ya, Mosina, T.V, Khomenko, O.I, Dudnik, E.V
• Format: Article
• Language: English
• Subjects: Aluminum compounds; Diffraction; Powders; X-rays
• ISSN: 1068-1302
• DOI: 10.1007/s11106-021-00222-4

Alumina-based nanocrystalline powders with different ZrO.sub.2 amounts were produced for the first time by hydrothermal synthesis in an alkaline environment for designing zirconia toughened alumina (ZTA) composites. In ZTA composites, ZrO.sub.2 solid solution particles codoped with ceria and yttria are distributed in a rigid Al.sub.2O.sub.3 matrix. To examine the physicochemical properties, 90 wt.% Al.sub.2O.sub.3-10 wt.% ZrO.sub.2 (Y.sub.2O.sub.3, CeO.sub.2) and 58.5 wt.% Al.sub.2O.sub.3-42.5 wt.% ZrO.sub.2 (Y.sub.2O.sub.3, CeO.sub.2) powders were used. The ZrO.sub.2 solid solution had composition 90 mol.% ZrO.sub.2-2 mol.% Y.sub.2O.sub.3-8 mol.% CeO.sub.2. The hydrothermal powders were heat treated in the temperature range 400-1450°C and examined by X-ray diffraction, differential thermal analysis, and electron microscopy. The powder specific surface area was determined by the BET method. The sizes of primary particles were determined with the Scherrer equation. The AMIC software (Automatic Microstructure Analyzer) was employed to process the morphology analysis results. The phase transformations and active sintering of the ZTA powders determined the dependences showing the sizes of primary particles and the specific surface area of the powders versus the heat treatment temperature. With higher ZrO.sub.2 content, temperature of the F-ZrO.sub.2 [right arrow] T-ZrO.sub.2 phase transformation decreased, the likelihood of M-ZrO.sub.2 to emerge increased, and the sequence of Al.sub.2O.sub.3 phase transformations changed after the boehmite had decomposed. The variation in the morphology and specific surface area of the powders in the heat treatment process indicated that their sintering activity increased. The dependence of the shape factor characterizing the nanocrystalline 90AZG and 58.5AZG powders on the heat treatment temperature was studied. The starting nanosized 90AZG and 58.5AZG powders had a similar distribution of agglomerates according to the shape factor. Round agglomerates and multifaceted regular agglomerates were predominant. The way in which the shape factor of the agglomerates varied with temperature was associated with a topochemical memory effect manifested by the 90AZG and 58.5AZG powders were examined. With increasing ZrO.sub.2 content, the microhardness of the ZTA composites decreased from 195 to 160 MPa, fracture toughness (KIc) increased from 6 to 8 MPa · m0.5, and Vickers hardness decreased from 8.3 to 5.6 GPa. The improvement in conso