Characterization of Flakes on Copper Bond Pad after Flux Cleaning Process

In this study, flakes were analysed using several imaging tools including optical scope, SEM & TEM which were complemented with EDX analysis for elemental investigation of the flakes. Flakes formed on copper bond pad after flux cleaning process were characterized due to the fact that there were...

Full description

Saved in:
Bibliographic Details
Main Authors: Ying, Lee Chai, Juerzen, Walter, Fei, Cheong Choke
Format: Conference Proceeding
Language:English
Subjects:
Cleaning
Copper
Flux Cleaning & Copper Bond Pad
Inspection
Lead
Metal flakes characterization
Optical imaging
Silver
Online Access:Request full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:In this study, flakes were analysed using several imaging tools including optical scope, SEM & TEM which were complemented with EDX analysis for elemental investigation of the flakes. Flakes formed on copper bond pad after flux cleaning process were characterized due to the fact that there were very few studies found in current literature. With in-depth analysis results interpretation of each method, a cross sectional schematic was proposed illustrating the interaction of flake on copper bond pad after flux cleaning process. Based on SEM & TEM analysis results, no evidence of IMC formation of the flake to copper bond pad was reported. From this flake characterization study, it was recommended to the assembly process experts to reduce or eliminate flakes formation on bond pad surface after flux cleaning process as accumulation of flakes on bond pad's surface would endanger robust wire bonding and also good adhesion quality and reliability assurance of semiconductor product in the long run.
ISSN:1946-1550
DOI:10.1109/IPFA.2018.8452611