Highly textured nanostructure of pulsed laser deposited IrO2 thin films as investigated by transmission electron microscopy

• Published in: Journal of materials research 2001-08, Vol.16 (8), p.2336-2342
• Main Authors: Serventi, A. M., El Khakani, M. A., Saint-Jacques, R. G., Rickerby, D. G.
• Format: Article
• Language: English
• ISSN: 0884-2914; 2044-5326
• DOI: 10.1557/JMR.2001.0320

Highly conductive iridium dioxide (IrO2) thin films have been deposited onto in situ oxidized Si(100) substrates by means of a reactive pulsed laser deposition (PLD) process. The polycrystalline IrO2 films were obtained by ablating a metal iridium target under an optimal oxygen background pressure of 200 mtorr and at different substrate deposition temperatures (Td ) ranging from 350 to 550 °C. Conventional and high-resolution transmission electron microscopy (HRTEM) techniques were used to investigate the micro- and nanostructural changes of the PLD IrO2 films as a function of their deposition temperatures. The microstructure and the morphology of the PLD IrO2 films was found to change drastically from an irregular and loosely packed columnar structure at Td = 300 °C to a uniform and densely packed columnar structure for higher Td (≥350 °C). For IrO2 films deposited in the 350 ≤ Td ≤ 550 °C range, HRTEM have revealed the presence of highly textured arrangements of almost spherical IrO2 nanograins (of 3–5 nm diameter, regardless of Td) in the columns (of which diameter was found to increase from 85 ± 15 to 180 ± 20 nm as Td increases from 350 to 550 °C). Lattice resolution and dark-field imaging have pointed out the presence of large IrO2 crystallites made of many similarly oriented nanograins (i.e., under the same Bragg diffraction conditions). Moreover, a high continuity of the lattice planes across the entire crystallite was clearly observed. This latter aspect together with the highly textured nanostructure of the IrO2 films correlate well with their high conductivity (42 ± 6 μω cm for Td ≥ 400), which was found to be comparable with that of bulk single-crystal IrO2.