Hydrogen oxidation kinetics on platinum-palladium bimetallic thin films for solid acid fuel cells

Solid acid fuel cells (SAFCs) based on the proton-conductive electrolyte CsH2PO4 have shown promising power densities at an intermediate operating temperature of ~250 °C. However, Pt loadings in SAFCs remain higher than desirable, and the electrocatalysis mechanisms in these devices are still unknow...

Full description

Saved in:
Bibliographic Details
Published in:APL materials 2018-12, Vol.7 (1)
Main Authors: Paik, Haemin, Berenov, Andrey V., Skinner, Stephen J., Haile, Sossina M.
Format: Article
Language:English
Subjects:
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Solid acid fuel cells (SAFCs) based on the proton-conductive electrolyte CsH2PO4 have shown promising power densities at an intermediate operating temperature of ~250 °C. However, Pt loadings in SAFCs remain higher than desirable, and the electrocatalysis mechanisms in these devices are still unknown. Here, hydrogen oxidation kinetics on Pt and Pt-Pd bimetallic thin film electrodes on CsH2PO4 have been evaluated to establish the potential for a beneficial role of Pd in SAFC anodes. Symmetric cells fabricated by depositing a metal film on both sides of electrolyte discs are characterized for studying hydrogen electro-oxidation across the gas|metal|CsH2PO4 structure. It was found that Pd reacts with CsH2PO4, forming palladium phosphide at the metal-electrolyte interface. Accordingly, the activity of Pd was examined in a bilayer geometry of Pd|Pt|CsH2PO4|Pt|Pd. The bilayer Pt|Pd films showed much higher activity for hydrogen electro-oxidation than films of Pt alone, as measured by AC impedance spectroscopy. Ex situ low energy ion scattering and scanning transmission electron microscopy revealed that Pd diffused into the Pt layer under operating conditions. The dramatic impact of Pd along with its presence throughout the film suggests that it catalyzes reactions at both the metal-gas and metal-electrolyte interfaces, as well as increasing hydrogen diffusion rates through the films.