XPS study of the PET film surface modified by CO2 plasma: effects of the plasma parameters and ageing
Chemical modification of the PET surface by carbon dioxide plasma treatment has been studied using X-ray photoelectron spectroscopy (XPS). The plasma process results mainly in the formation of carbonyl, carboxyl, and carbonate groups at the PET surface. Under rather mild treatment conditions (low pl...
Saved in:
Published in: | Journal of adhesion science and technology 1997-01, Vol.11 (5), p.735-751 |
---|---|
Main Authors: | , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Chemical modification of the PET surface by carbon dioxide plasma treatment has been studied using X-ray photoelectron spectroscopy (XPS). The plasma process results mainly in the formation of carbonyl, carboxyl, and carbonate groups at the PET surface. Under rather mild treatment conditions
(low plasma power combined with a short treatment time), the formation of C-O bonds was found to be dominant, whereas the formation of highly oxidized carbon or double-bonded oxygen-containing groups required a high plasma power or a relatively long treatment time. The treatments performed
under excessive conditions frequently led to degradation at the polymer surface. Angle-resolved XPS analyses performed on a freshly modified PET film showed a slight decrease in the O/C atomic ratio when the take-off angle (TOA) increased, indicating a relatively uniform distribution of oxygen
within the sampling depth (estimated to be about 8 nm at 80° TOA). The chemical composition of the plasma-modified surface was found to be relatively stable on extended storage in air under ambient conditions. The decrease in oxygen-containing groups at the carbon dioxide-plasma-treated
PET surface upon ageing is mainly ascribed to the surface rearrangement of macromolecular segments, the loss of oxygen-containing moieties introduced by the plasma treatment, and the possible migration of non-affected PET chains from the bulk to the surface region. |
---|---|