Effect of supercritical CO2 pre-treatment and kiln-drying of fresh green Pinus radiata sapwood on kiln brown stain and drying stress

• Published in: Wood science and technology 2022-07, Vol.56 (4), p.1127-1148
• Main Authors: Dawson, Bernard S. W., Sargent, Rosie, Riley, Steve G., Husheer, Sean, Simpson, Ian G.
• Format: Article
• Language: English
• Subjects: Biomedical and Life Sciences; Brown stain; Carbon cycle; Carbon dioxide; Ceramics; Color; Composites; Conditioning; Dewatering; Drying; Glass; High pressure; Kilns; Life Sciences; Machines; Manufacturing; Moisture content; Moisture effects; Moisture gradient; Natural Materials; Original; Pine trees; Pinus radiata; Pretreatment; Processes; Residual stress; Schedules; Steam; Water content; Wood Science & Technology
• ISSN: 0043-7719; 1432-5225
• DOI: 10.1007/s00226-022-01399-6

High pressure (20 MPa), cyclic, supercritical carbon dioxide (scCO 2 ) treatments can reduce the moisture content of green Pinus radiata sapwood from 150–200% to 35–40%. Such treatments can be used as a dewatering pre-treatment before the kiln-drying of timber. Kiln-drying can utilise various temperature and humidity schedules, targeting around 10% moisture content, with a final stress-relieving steam-conditioning step. After scCO 2 treatment and kiln-drying of samples, kiln brown stain was evaluated using the CIE L*a*b* colour space while drying stress was assessed by stress-cup measurements. The most significant results of scCO 2 pre-treatment of Pinus radiata sapwood followed by kiln-drying plus steam-conditioning were as follows: Drying from green (36 h from a moisture content (MC) of 164%) using a conventional temperature schedule (90 °C/60 °C) took 2–5 times longer than kiln-drying scCO 2 pre-treated boards (37.5% MC) to a target of 10% MC. Colour measurements proved that kiln brown stain does not occur. The use of a steam-conditioning step in reducing internal drying stresses was important irrespective of whether or not there was a scCO 2 pre-treatment step. Over all drying schedule combinations, internal drying stress of both green and scCO 2 pre-treated timber was similar after kiln-drying plus steam-conditioning. However, using only 90 °C/60 °C schedule data, with steam-conditioning, drying stresses were lower using kiln-drying without the scCO 2 pre-treatment. This was surprising since the scCO 2 step reduced the moisture content to around 37.5% without significant moisture gradients and so a secondary kiln-drying to 10% moisture content could have been expected to yield lower internal stress levels by preventing large moisture gradients to develop during drying. This result confirms the efficacy of the steam-conditioning step following standard kiln-drying. The colour data demonstrating the prevention of kiln brown stain using kiln-drying schedules offers a path to increasing timber quality for interior applications.