Thermal degradation in methylammonium-formamidinium-guanidinium lead iodide perovskites

The stability of hybrid halide perovskites (HPs) is one of the main factors hindering their potential commercial application. Numerous environmental agents are known to degrade HPs and their devices, including temperature, which can cause chemical modifications even at operational temperatures. Ther...

Full description

Saved in:
Bibliographic Details
Published in:Journal of materials chemistry. C, Materials for optical and electronic devices Materials for optical and electronic devices, 2024-04, Vol.12 (14), p.5138-5149
Main Authors: Minussi, F. B, Silva, R. M, Carvalho, J. F, Araújo, E. B
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The stability of hybrid halide perovskites (HPs) is one of the main factors hindering their potential commercial application. Numerous environmental agents are known to degrade HPs and their devices, including temperature, which can cause chemical modifications even at operational temperatures. Thermal degradation has been the subject of major studies in pure and HP-related compounds that have paved the way for a deep understanding of the phenomenon. However, thermally induced modifications in mixed-cation HPs have not been addressed in detail yet. In the present work, we report a systematic study of thermal degradation over a wide range of compositions of methylammonium lead iodide (MAPbI 3 ) partially substituted by guanidinium (GA + ) and formamidinium (FA + ), using diverse experimental techniques and thermal treatment conditions. The results indicated that mixed-cation HPs were more stable than pure MAPbI 3 . Thermal degradation followed the volatilization of MA + and MA + -related chemical species with PbI 2 consequently appearing; however, GA + -rich compositions could suffer from an additional degradation pathway by the segregation of non-perovskite GAPbI 3 , reducing the material's thermal stability. This process also provoked a change in the degradation kinetic law. Remarkably, the simultaneous substitution with FA + inhibited the formation of GAPbI 3 , even in compositions with high GA + contents. Our work advances the crucial understanding of thermal degradation processes and how to increase the thermal stability of halide perovskites. Thermal degradation experiments in GA x FA y MA 1− x − y PbI 3 perovskites show that mixed compositions are generally more stable, but not always. Large GA + cations may decrease the stability and even change the order of the degradation kinetics.
ISSN:2050-7526
2050-7534
DOI:10.1039/d4tc00395k