The electrocatalytic properties of an IrO2/SnO2 catalyst using SnO2 as a support and an assisting reagent for the oxygen evolution reaction

Electrocatalysts made of IrO2/SnO2 were prepared using the Adams method for solid polymer electrolyte (SPE) water electrolysis. The physicochemical properties of the catalyst were characterized via X-ray diffraction (XRD) and transmission electron microscopy (TEM). The electrochemical properties of...

Full description

Saved in:
Bibliographic Details
Published in:Electrochimica acta 2012, Vol.59, p.105-112
Main Authors: Xu, Junyuan, Liu, Gaoyang, Li, Jianling, Wang, Xindong
Format: Article
Language:English
Subjects:
Alternative fuels. Production and utilization
Applied sciences
Catalysts
Electrochemical impedance spectroscopy
Electrolysis
Energy
Exact sciences and technology
Fuels
Hydrogen
Iridium
Mass ratios
Platinum
Tin dioxide
Tin oxides
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Electrocatalysts made of IrO2/SnO2 were prepared using the Adams method for solid polymer electrolyte (SPE) water electrolysis. The physicochemical properties of the catalyst were characterized via X-ray diffraction (XRD) and transmission electron microscopy (TEM). The electrochemical properties of the catalyst were investigated using cyclic voltammetry (CV), electrochemical impendence spectroscopy (EIS), chronopotentiometry and Tafel curve measurements in 0.1 mol L-1 H2SO4 at room temperature. The test results showed that the catalytic properties of IrO2/SnO2 depended on the mass ratio of iridium to tin, and that the optimal mass ratio was 2:1. The optimized catalyst was applied to a membrane electrode assembly (MEA), and the stationary current-potential relationships were determined. With an IrO2/SnO2 (2:1) anode, a 40% Pt/C cathode and a total noble metal (Ir, Pt) loading of 1.2 mg cm-2, the terminal applied potential difference of the water electrolysis was 1.70 V at 2 A cm-2 and 80 degree C.
ISSN:0013-4686
1873-3859
DOI:10.1016/j.electacta.2011.10.044